EAA 3004乙烯丙烯酸共聚物
发布日期:2020-01-02     浏览量:554

PRIMACOR™ 3004 Copolymer

陶氏塑料

产品说明

PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack

and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This

resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR).

Excellent draw down and edge stability

Excellent product resistance

Excellent hot tack, heat seal, toughness

High performance sealant or tie layer

Complies with:

U.S. FDA 21 CFR 177.1310(b)

EU, No 10/2011

Consult the regulations for complete details.

总体

材料状态 • 已商用:当前有效

供货地区 • 亚太地区

机构评级 • EU No 10/2011 FDA 21 CFR 177.1310 (b)

形式 • 颗粒料

物理性能 额定值 单位制 测试方法

比重 0.938 g/cm³ ASTM D792

ISO 1183

熔流率 2 (190°C/2.16 kg) 8.5 g/10 min ASTM D1238

ISO 1133

共聚单体含量 3 9.7 %

机械性能 额定值 单位制 测试方法

抗张强度 ASTM D638

ISO 527-2

屈服, 模压成型 7.93 MPa

断裂, 模压成型 17.6 MPa

伸长率 (断裂, 模压成型) 600 % ASTM D638

ISO 527-2

热性能 额定值 单位制 测试方法

维卡软化温度 81.1 °C ASTM D1525

ISO 306

溶融温度(DSC 98.0 °C Internal Method

挤出 额定值 单位制 测试方法

熔体温度 260 290 °C

内缩量 (288°C, 25.4 µm) 50.8 mm Internal Method

最小涂层厚度 10 µm Internal Method

最小涂层重量 9.8 g/m² Internal Method

挤压说明

挤出涂层薄膜的制造条件:

用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。

• 螺杆尺寸:3.5 英寸 (89 mm)30:1 L/D

• 模具:30 英寸模具切边至 24 英寸

• 模具间隙:20 密尔 (0.508 mm)

• 熔体温度:550°F (288°C)

• 输出:250 /小时

• 气隙:6 英寸 (152 mm)

备注 1  一般属性:这些不能被视为规格。

2  如同在生产时测量的一样。 